On the base of N.N. Blokhin Russian Cancer Research Center of RAMs had been designed the method of acquiring sterile deimmunized matrix from donor bone. This matrix can be used as a base for bioimplants for replacing bone defects. The aim of the research was the estimation of influence of the chemical treatment to the bone mechanical properties and the suppression of acute implant rejection. It was proved that the method provides sterilization and decreases immunogenicity of the matrix (absence of any degradation signs and absence of rejection reaction spreading during syngenic heterotopic transplantation in mice). After applying this method, we do not observe any signs of decreasing of mechanical properties (yield stress, Young's modulus, ultimate stress) in comparison with intact bone.
На базе ФГБУ «РОНЦ им. Н.Н. Блохина» РАМН был разработан метод получения из донорской кости стерильного деиммунизированного матрикса, который может быть использован в качестве основы биоимплантатов для замещения дефектов костной ткани. Целью исследования являлась оценка воздействия предлагаемого способа химической обработки на прочностные характеристики костей, а также на подавление развития реакции острого отторжения организмом реципиента при имплантации. Было доказано, что предлагаемый способ обеспечивает стерилизацию матрикса и снижает его иммуногенность, что проявляется в отсутствии признаков деградации и развитии реакции острого отторжения при сингенной гетеротопной имплантации мыши. При этом в результате применения данного способа получения костного матрикса в сравнении с исходной костью не наблюдается снижения прочностных характеристик, оцениваемых по показателям «предел текучести», «модуль упругости» и «предел прочности».